1214 is a free machining low tensile, low hardenability carbon steel, with free machining characteristics due to the addition of Sulphur. The addition of Sulphur makes welding of this material difficult. 1214 is generally only used in the as rolled condition, and then either cold drawn or turned to allow feeding through NC machines. 1214 can be carburised achieving surface hardness of around 60HRC in smaller sections, however this will reduce as section size increases. Core strength will, however, remain low. 1214 is not recommended for flame, induction or nitride hardening.
Typical applications included lightly stressed components, and machinery parts.